Induction hardening is being increasingly used within the gear industry. However, before looking at the advantages of the method, it is helpful to review the basics of the technology. The phenomenon of induction heating begins by passing an alternating current through a coil in order to generate a magnetic field. The strength of the field varies in relation to the strength of the current passing through the coil. The field is concentrated in the area enclosed by the coil, while its magnitude depends on the strength of the current and the number of turns in the coil. (Figure 1)
Please visit our website for more information on this topic.
Eddy currents are induced in any electrically conductive object, a metal bar, for example, placed inside the coil. The phenomenon of resistance generates heat in the area where the eddy currents are flowing. Increasing the strength of the magnetic field increases the heating effect. However, the total heating effect is also influenced by the magnetic properties of the object and the distance between it and the coil. (Figure 2)
The eddy currents create their own magnetic field that opposes the original field produced by the coil. This opposition prevents the original field from immediately penetrating to the center of the object enclosed by the coil. The eddy currents are most active close to the surface of the object being heated, but weaken considerably in strength towards the center. (Figure 3)
The distance from the surface of the heated object to the depth where current density drops to 37% is the penetration depth. This depth changes in relation to various parameters such as heating times, initial material and choice of frequency.
Key features of induction hardening are fast heating cycles, accurate heating patterns and cores that remain relatively cold and stable. Such characteristics minimize distortion and make heating outcomes extremely repeatable, reducing post-heat processing such as grinding. This is especially true when comparing induction hardening to case carburizing.
Induction hardening also reduces pre-processing, as the geometry changes are less than those caused by carburizing. Such minimal changes mean distortion does not need to be accounted for when making the gear. With gears destined for gas carburizing, however, &#;offsets&#; that represent distortion are often introduced at the design stage. These intentional offsets compensate for distortion caused during the lengthy heat soaks typical of carburizing.
Induction can heat precisely localized zones in gears. Achieving the same degree of localized hardening with carburizing can be a time- and labor-intensive procedure. When carburizing specific zones such as the teeth areas, it is usually necessary to mask the rest of the gear with &#;stop off&#; coatings. These masks must be applied to each and every work piece, and removed following the hardening process. No such masking is necessary with induction hardening.
Induction hardening is ideal for integrating into production lines. Such integrated &#;inline&#; hardening is more productive than thermo-chemical processes. Moreover, integrated hardening minimizes costs, as the gears do not have to be removed for separate heat treatment. In fact, induction heating makes it possible to create one seamless production flow through the machining, hardening, quenching, tempering and storage stages.
The induction heating method used for small- and medium-sized gears is often referred to as &#;spin hardening&#;. This is because the gear is placed within an induction coil and spins as the eddy currents are induced. Spin hardening can in turn be divided into two main methods: through hardening and contour hardening. With the first method&#;used primarily for gears exposed to high wear&#; the tooth perimeter is hardened with a low specific power. However, if the frequency is too low, there is the risk that above the Curie temperature the induced eddy current flows mainly in the root circle, and the temperature lags behind in the teeth. Quenching is either by submersion or spraying, and is usually delayed in order to achieve a uniform temperature between the teeth and the root circle. Tempering after through-hardening is essential in order to prevent later cracking.
Contour hardening is divided into single- and dual-frequency processes. With the former, a single generator feeds the inductor. Austenitizing is achieved either in a single heating, or by pre-heating the gear to 550-750° C before heating it to the hardening temperature. The purpose of pre-heating is to reach an adequately high austenitizing temperature in the root circle during final heating, without overheating the teeth tips. Short heating times and a high specific power are usually required to achieve hardening profiles at an irregular distance to the tooth face.
The dual-frequency process uses either separate or simultaneous frequencies. Using separate frequencies achieves hardening profiles similar to case hardening. The process applies two different frequencies one after the other to the gear. The teeth are pre-heated at a low frequency to 550-750° C. The frequency should be such that pre-heating occurs in the root circle area. After a short delay, use of a higher frequency and specific power achieves austenitizing. Accurate monitoring systems are essential, as heating times are measured in tenths of seconds or seconds during this final heating phase.
With the simultaneous dual-frequency method, a lower and a higher frequency feed into the inductor at the same time. Hardening is achieved by heating the root circle with the lower frequency, and the tooth tips with the higher (see Figure 4). Unlike the separate, or stepped, dual-frequency process, pre-heating is not always required when using the simultaneous dual-frequency process. However, the short heating times used with simultaneous frequencies place high demands on the generator and machine engineering. Figure 5 shows an example of a hardening profile achieved with this method.
Correct quenching is critical for perfect spin hardening results, and should be performed as soon as possible after the final heating. The time gap between heating and quenching can be minimized by using a fast CNC axle to position the spray head, or by integrating a quench circuit into the inductor. During the quenching phase the rotational speed of the gear is decreased to below 50 rpm to avoid a &#;shadow effect&#; on the flank opposing the direction of rotation.
Many other factors influence spin hardening outcomes. The material to be hardened and its initial structure, for example, have a decisive impact. Due to short austenitizing times, the initial steel structure must be close-grained (ASTM 7 and above). Non-homogenous pearlite-ferrite initial structures are not suitable. The importance of initial structure and carbon content increases as module size decreases. If a somewhat increased quenching distortion is acceptable, inductive pre-quenching and tempering prior to contour hardening can greatly improve the gear&#;s hardenability.
Module size is another key factor in spin hardening. For the dual frequency method with simultaneous frequencies, the range is 2.2 < m &#; 5mm. However, for cost reasons the gear diameter should be limited to approximately d &#; 250mm. For modules of m &#; 3.0mm, the separate dual frequency method is preferred. This is because a final hardening phase with only the higher frequency achieves better hardening at an irregular distance to the face. The single frequency method is almost exclusively used for internal ring gears with a module where m &#; 1.25mm, such as those frequently used in automotive automatic transmission systems.
Spin hardening is a versatile and reliable process that can harden spur-toothed, helical spur and internal gears at an irregular distance to the face. However, different gear forms influence hardening results. With helical gearing, an asymmetrical hardening of the tooth flank at a depth of up to 2-3mm from the gear face has to be accepted. This situation is however only pronounced with helix angles of β &#; 28°. Patented coil solutions are available that limit this effect by enhancing power distribution.
Correctly designed and built induction coils are absolutely critical for successful, cost-effective induction heating. In fact, designing and testing coils is often the process with the longest lead time when devising an induction heating solution. A key reason for this is the fact that coils are task specific. They must be designed to achieve specific results on specific materials under specific conditions. There are no&#;or at least there shouldn&#;t be&#;&#;off-the-shelf&#; coil designs.
Rigorous testing of a coil&#;s design and construction is essential. Too few people realize that coils are often the part most exposed to harsh operating conditions. Testing and computer-aided simulation is therefore sometimes needed to arrive at a design that is both safe and fatigue resistant. And of course, it takes repeated testing to achieve optimal part-heating patterns.
Nothing can be taken for granted when designing induction coils. With very high power density coils, for example, one even needs to determine the correct speed at which cooling water should flow through the coil. Too low a speed will result in insufficient thermal transference. But even when the correct speed has been found, the coil designer must decide whether a booster pump is necessary in order to achieve and maintain the desired water through-flow rate. The competent coil designer will also specify a purity level for the cooling water, in order to minimize corrosion on the inside of the coil. So something as apparently straightforward as the coil&#;s water, is in fact a complex matter demanding technical competence and specialist equipment.
Magnetic flux concentrators are another area of an overall induction solution that at first glance seems relatively straightforward. As the name suggests, the main function of such concentrators is to concentrate the coil&#;s current in the area of the coil facing the work piece. Without a concentrator, much of the magnetic flux is free to propagate around the coil. This uncontrolled flux will then &#;engulf&#; adjacent conductive components. But when channeled by a concentrator, the magnetic flux can be restricted to precisely defined areas of the work piece, resulting in the localized heating zones characteristic of induction heating.
Many variables must be considered when making flux concentrators. The work piece&#;s material, the coil&#;s shape, the application&#;each influences the concentrator&#;s final design. Even deciding what material to use for the concentrator can be a complicated task. Basically, concentrators are made from laminations, or from pure ferrites and ferrite- or iron-based powders. Each concentrator material has its own drawbacks and advantages. Laminations have the highest flux densities and magnetic permeability; they are also less expensive as parts than iron- and ferrite-based powders. Laminations must however be stamped to a few standardized sizes and are therefore less flexible. They are also labor intensive to mount.
Pure ferrites can also offer outstanding magnetic permeability. However, they suffer from low saturation flux density, and their brittleness makes them difficult to machine (diamond-tipped cutters must be used). Iron powders are easy to shape, offer high flux densities, and are easy to shape. But great care must be taken to provide against over-heating, as internal losses or heat transfer from the heated part means such powders have a relatively low working temperature.
Of course, many other factors need to be considered when designing induction coils. Correct impedance matching between the coil and the power source, for instance, is crucial in order to use the full power from the power source. Plus the fact that coils need five to ten times as much reactive as active power.
As we have seen, a professionally designed and fabricated induction coil is an advanced, complex component. Unfortunately, too many induction users persist in viewing coils as low-tech copper tubes. The results of this misconception are incorrect and even dangerous coil designs, amateurish repairs, insufficient or incorrect maintenance, and ultimately, process and equipment failures.
If you want to learn more, please visit our website Duolin.
INDUCTION HEATING
INDUCTION HEATING is the heating of materials by electromagnetic action. A voltage is induced into a conductive component and the losses from the resulting current flows are seen as heat.
When an alternating current flows through a coil (inductor) a varying magnetic field is set up around and within the coil. When the coil surrounds or is near a conductive material (workpiece), the varying magnetic field links with and induces a voltage in the workpiece. The resulting current flows can be isolated eddy currents set up within the workpiece or circulating currents based on transformer action.
The inherent electrical resistance of the material to the current flow (I 2 R losses) results in the heating of the workpiece. A well-designed induction heating installation considers the properties of the material to be heated including resistivity, permeability (magnetic properties), part geometry, mass, and required heating rate. The characteristics of the induction installation are then selected to satisfy the heating requirement. Operational frequency, power rating, output head configuration, power density, and overall efficiency are considered.
Advantage of Induction Heating Process :
NON CONTACT HEATING
The heating of materials takes place without physical contact. Heating remains consistent without being affected by variables, such as contact resistance or the rate of heat transfer through changing surface conditions. Heating can take place in protective atmospheres or directly through coatings. The magnetic field does not affect nonconductive materials like plastic or ceramic. The photo shows an induction coil selectively heating components in a brazing operation, while they are fixtured inside a bell jar with an inert gas atmosphere.
SAFE AND FLAMELESS
Induction heating does not require an open flame, hot air blast, radiant heat, or hot soldering iron to endanger or cause discomfort to the operator or obscure the process. Non-conductive materials are not affected and can be near the heating zone without damage. The large terminal at right is soldered quickly and without damage to the insulation.
PRECISE HEAT INPUT
Heating coils are configured to precisely heat the location required. Varying coil shape, distance from the workpiece, and turn spacing allows for the even heating of parts by compensating for differences in mass and materials. An example is a shaped coil which evenly heats a rifle bolt handle and bolt. A correct heat pattern is achieved by forming the coil to a specific shape on the basis of experience and experiment.
REPEATABLE
Heating is identical cycle to cycle and part to part. Variations in incoming power are automatically compensated for. No warmup time is required. Timed cycles provide consistent results. This catheter tipping operation is an example of a process which requires exact heat input to assure a uniform product.
ELECTRONIC CONTROL
Solid state induction heating allows instantaneous heat on or heat off. Power levels can be varied throughout the heating cycle. Closed loop interface of a process using standard PLCs or temperature controllers is easily accomplished. For instance, tools can be brazed by starting with a low power heat to dry applied flux. This is followed by full power to rapidly achieve brazing temperature and finally a reduction in power to hold briefly at brazing temperature without overheating.
ECONOMICAL
Induction heating, when all costs are weighed, is often the best and most profitable heating alternative for the long term. Energy is directed only to the part to be heated and achieves much higher efficiency than fossil fuels or radiant heating systems. No warmup time is required, no changing of tanks, or leaving heat on when parts are not present. Failure rates are reduced when heating operations maintain consistency. Jobs like brazing fittings to tanks can be done reliably unit after unit without the need of a skilled operator.
Induction Brazing :
Induction heating is used to heat metals to be joined until a brazing alloy which is placed inside or in proximity to the joint, along with a fluxing agent, melts and creates a bond between the metals. The ability of induction heating to provide a controlled heat input and heat pattern with consistency greatly reduces the skill level required to produce joints of good quality and appearance. Across International Induction furnaces are used for brazing carbide to steel, PCD and CBN to holders, tube fittings and electrical contacts.
Across International is manufacturer of induction melting furnaces is the go-to place for high-quality.
Whether you&#;re looking for an induction melting furnace, a gold melting furnace, or accessories /spare parts for your induction heating equipment, Across International has what you need. For more information on our metal melting furnaces and replacement parts for your steel melting induction furnaces, contact Across International today.